Water base Conformal Coating

Download Catalogue

Download Catalogue

Download Catalogue



AQUACOAT "CONW-54"


We are Manufacturer, Supplier, Exporter of Water base Conformal Coatings and our setup is situated in Pune, Maharashtra, India. Majorly we serve our products to customers from Hong Kong, Thailand, Vietnam, China, Singapore, Malaysia, Sri Lanka.
AQUACOAT "CONW-54" is VOC free moisture proof coating material for PCB. It is veryenvironmentally-friendly because it contains water as solvent instead of organic solvent, and also keep have high property such as low coefficient of elasticity, heat resistance, high insulation property.

 

Water base Conformal Coating

Technical Data Sheet

 

Items

Unit

CONW-54

Measurement method

Aspect

-

Liquid with milky white color

-

Solvent

-

lon exchange water

-

Regulation by lows

-

None

-

Solid ratio

%

40

120°CX1hr

Viscosity

mPa s

12

25°C

Thinner

-

lon exchange water
(Usually No Need)

-

Yound module

23°C

Mpa

9.2

Tension speed :
1 0mm/min

-40°C

270

Elongation

23°C

%

500

Tension speed :
300mm/min

-40°C

40

Moisture transmission

g/m2/ 24H

35

40°C x90%
thickness:1OOpm

Insulation resistance

After 1000hr

2.5E+09

85°C x 85% RH 0.3mm pitch comb-type electrode), thickness: 0.02mm  Voltage: 15V

After 2000hr

2.2E+09

Time to dry with touch

min.

15

thickness:0.02mm

Recommendation
for drying condition

-

50-90°C x
5-10min.5-10min.

-

GLOBAL QUALITY THROUGH INDO-JAPAN  TECHNOLOGY

 

 

 

1

Test Specification

As Per ASTM B 117-2011

2

Salt Solution

5% NaCI Solution

3

Type of the Salt

NaCI Analytical Grade

4

Type of Water

Distilled Water

5

Test Temperature

35 ± 1 deg C

6

Fog Collection Rate

1.3 mVhr (Average)

7

pH of collected Solution

7.2

8

Exposure period

72 Hrs.

 

2.0BSERVATIONS

 

Sr.No

Sample ID

After 72 Hrs

1

CONW-54

On panel

No corrosion Observed

2

(Water Base Conformal Coating)

On Metal

No corrosion Observed

 

 

Sr.No 

Test Condition

Observation

1

At 35°C, 90 ± 5% RH for 24 Hrs

No Corrosion, Crack or discoloration observed

2

At 65°C, 90 ± 5% RH for 24 Hrs

No Corrosion, Crack or discoloration observed

 

Note: Both test conditions were performed on same Conins Make CONW-54 Coating sample.


3.0 COATING THICKNESS

 

Sr.No

Sample ID

Coating Thickness

1

Single Coat

110

2

Double Coat

145

3

Three Coat

185

 

4.0 APPEARANCE
i) No bubbles, pin holes, whitish Spots, Blistering, wrinkling and peeling observed.

5.0 SCRATCH TEST
(250 gm load,1 mm Dia.Ball)

 

Sr.No

Sample ID

Observation

1

54 Coating

No Scratch Noted